Compressive Strength

ASTM C170/C179M-17

Dry condition: 238MPa Wet condition: 244MPa

Point Impact

CSA B45.5-17/IAPMO Z124-2017

No cracks or chips on surface

Stain Resistance Test

ANSI Z124.6-2007

Stain resistance rating: 50 The masimum stain depth" 0.057mm

Colourfastness Test

ASTM D2244-23 D65-10 25mm

3

Abrasion Resistance

ASTM C241/C241M-15e1

39.6

Flexural Strength

ASTM C880/C880M-15

Dry condition: 58.8MPa Wet condition: 67.3MPa

Impact Resistance

EN 14617-9:2005

> 11.86J

Absorption and Bulk Specific Gravity

ASTM C97/C97M-18

Water absorption: 0.02% Bulk specific gravity: 2.26

Density

ASTM D792-20 Method A

2.42g/cm³

Boiling Water Resistance

ANSI NEMA LD 3-2005 Section 3.5

No effect

Resistance to Freeze-Thaw Cycling

ASTM C1026-13(2018)

No cracking, disintegration or spalling weight loss:0.06%

Moh's Hardness

EN 101:1991

Moh's Hardness 6~7

Water Absorption

ASTM C373-18

0.04%

Rockwell Hardness

ASTM D785-08(2015) Procedure A

115M

Coefficient of Linear Thermal Expansion

ASTM D696-16

10.730 x 10⁻⁶/ᵒC

Dimensional Stability

EN 14617-12:2012

Verical displacement: 0.02mm

Chemical Resistance

En14617-10:2012

C4

Linear Shrinkage and Coefficeint of Thermal Expansion

ASTM C531-00

36 x 10⁻⁶/ᵒC

Linear Thermal Expansion Coefficient

ISO10545-8:1994

35 x 10⁻⁶/ᵒC

Radioactivity

GB 6566-2010

Class A

Slip Resistance

EN 14231:2003

56(Dry) 18(Wet)

Thermal Shock Resistance

EN 14617-6:2012

Mass loss: 0.04% Appearance: No visible defects Flexural strength after thermal shock: 34.4Mpa Flexural strength loss: 4.53%

Tactiliy/Visibility

EN 15285:2008 Section 4.2.12

No surface corrugation obtained by mechinical finishing

Thermal Conductivity

EN 12664:2001

0.383W/(m.k)